醫療級TPE,TPE 35A,醫療護理用品, ISO 10993 Part 5, ISO 10993 Part 4, USP 第 VI 類

Versaflex™ HC 2110-35N EU

熱塑性彈性體

 

普立萬公司

 

Technical Data

 

產品說明

Versaflex™ HC 2110-35N EU is a thermoplastic elastomer developed as an alternative to traditional isoprene rubber solutions for infusion stoppers & septums that require multiple needle penetration with good resealing performance. Versaflex™ HC 2110-35N EU addresses needs such as low piercing force and good spike retention.

• Overmolds to PP and PE. 

• Approved to ISO 10993 - 4 & 5 

• Approved to USP VI 

• Approved to USP 381 

 

總覽

材料狀態 • 已商用：當前有效

資料 1 • Technical Datasheet

搜索 UL 黃卡 •  普立萬公司

• Versaflex™

供貨地區 • 北美洲 • 拉丁美洲 • 亞太地區

• 非洲和中東 • 歐洲

特性 • 好的消毒性 • 良好的加工穩定性 • 良好的著色性

• 良好的成型性能 • 良好的流動性 • 脫模性能良好

用途 • 包覆成型 • 密封件 • 膜

• 插頭 • 密封裝置 • 醫療/護理用品

機構評級 • ISO 10993 Part 4 • ISO 10993 Part 5 • USP 第 VI 類

RoHS 合規性 • RoHS 合規

外觀 • 自然色

形式 • 粒子

加工方法 • 注射成型

物理性能 額定值(英制) 額定值(公制) 測試方法

密度 / 比重 0.902 0.900g/cm³ ISO 1183

彈性體 額定值(英制) 額定值(公制) 測試方法

抗張強度 (斷裂, 73°F (23°C)) 580psi 4.00MPa DIN 53504-S2

伸長率 (斷裂, 73°F (23°C)) 640% 640% DIN 53504-S2

壓縮永久變形 ISO 815

73°F (23°C), 72 hr 23% 23%

158°F (70°C), 22 hr 35% 35%

212°F (100°C), 22 hr 54% 54%

硬度 額定值(英制) 額定值(公制) 測試方法

肖氏硬度 (邵氏 A) 35 35 ASTM D2240

充模分析 額定值(英制) 額定值(公制) 測試方法

表觀粘度 (392°F (200°C), 11200 sec^-1) 10.2Pa·s 10.2Pa·s 內部方法

注射 額定值(英制) 額定值(公制)

建議的最大回制料比例 20% 20%

料筒后部溫度 360 到 380°F 182 到 193°C

料筒中部溫度 430 到 460°F 221 到 238°C

料筒前部溫度 460 到 480°F 238 到 249°C

射嘴溫度 460 到 480°F 238 到 249°C

加工（熔體）溫度 450 到 480°F 232 到 249°C

模具溫度 60 到 90°F 16 到 32°C

背壓 0.00 到 80.0psi 0.00 到 0.552MPa

螺桿轉速 80 到 200rpm 80 到 200rpm

 

Versaflex™ HC 2110-35N EU

熱塑性彈性體

普立萬公司

 

注射說明

Color concentrates with polypropylene (PP), ethylene vinyl acetate (EVA), or polyethylene (PE) carriers are most suitable for coloring Versaflex™ HC 2110-35N EU. Improved color dispersion can be achieved by using higher melt flow concentrates (with a melt flow from 25 - 40 g/10 min). Typical loadings for color concentrates are 1% to 5% by weight. Liquid color can be used, but mineral oil based carriers may have a significant effect on the final hardness value. Concentrates based on PVC should not be used. A high color match consistency can be obtained by using precolored compounds available from GLS. The final determination of color concentrate suitability should be determined by customer trials.

 

Purge thoroughly before and after use of this product with a low flow (0.5 - 2.5 MFR) polyethylene (PE) or polypropylene (PP).

 

Regrind levels up to 20% can be used with Versaflex™ HC 2110-35N EU with minimal property loss, provided that the regrind is free of contamination. To minimize losses during molding, the melt temperature should remain as low as possible. The final determination of regrind effectiveness should be determined by the customer.

 

Versaflex™ HC 2110-35N EU has excellent melt stability. Maximum residence times may vary, depending on the size of the barrel. Generally, the barrel should be emptied if it is idle for periods of 8 - 10 minutes or longer.

 

Drying is not Required

 

Injection Speed: 1 to 3 in/sec

1st Stage - Boost Pressure: 800 to 1200 psi 2nd Stage - Hold Pressure: 40-70% of Boost Hold Time (Thick Part): 2 to 5 sec

Hold Time (Thin Part): 1 to 4 sec

 

 

 

 

 

 

TPE Versaflex™ HC 2110-35N EU ,熱塑性彈性體TPE,包膠熱塑性彈性體TPE,包膠PP熱塑性彈性體TPE,包膠PA尼龍熱塑性彈性體TPE,包膠PA6熱塑性彈性體TPE,包膠PA66熱塑性彈性體TPE,包膠POM熱塑性彈性體TPE,包膠PE熱塑性彈性體TPE,包膠ABS熱塑性彈性體TPE,包膠PC+ABS熱塑性彈性體TPE,包膠PC熱塑性彈性體TPE,包膠PS熱塑性彈性體TPE,包膠ASA熱塑性彈性體TPE,包膠PMMA熱塑性彈性體TPE,包膠SAN熱塑性彈性體TPE,包膠PBT熱塑性彈性體TPE,包膠PPO熱塑性彈性體TPE,包膠熱塑性彈性體TPE是東莞市雙幫塑膠原料有限公司常年銷售的塑料,因為塑料價格行情每天都有新變化前天的報價不等于今天的報價。本公司銷售的所有原料保證是原廠原包,隨料可以提供生產廠商提供的物性表,SGS報告,COA原料出廠報告,REACH報告,SVHC報告,生物兼容報告,UL黃卡,提供原料注塑加工工程中可能出現的各種異常現象解決方法，塑料牌號太多，本網站沒有提供的本公司也有代理，詳情請咨詢本公司相關業務人員0769-87795123，微信：13549213581  QQ：15397858    13549213581 肖生