TPE 50A, 包覆成型, 墊圈, FDA食品接觸

 

GLS 422-126

熱塑性彈性體

 

吉力士（GLS）公司，熱塑性彈性體部門

 

Technical Data

 

產品說明

GLS 422-126 is designed to pass several fatty food extraction conditions identified in EU Directive 10/2011 and may be appropriate where FDA and EU 10/2011 compliances are required.

GLS 422-126 will also overmold and co-extrude to polypropylene.

 

 

總體

 

材料狀態 • 已商用：當前有效

資料 1 •  Technical Datasheet

搜索 UL 黃卡 •  GLS

供貨地區 • 歐洲

特性 • 食品接觸的合規性

用途 • 包覆成型 • 墊圈 • 容器

• 廚具 • 非特定食品應用 • 消費品應用領域

機構評級 • FDA 21 CFR 177.1210 2 • 歐洲 10/1/2011 12:00:00 AM 2

RoHS 合規性 • RoHS 合規

外觀 • 半透明

形式 • 粒子

加工方法 • 擠出 • 注射成型

物理性能 額定值(英制) 額定值(公制) 測試方法

比重 0.900 0.898g/cm³ ISO 1183

彈性體 額定值(英制) 額定值(公制) 測試方法

拉伸應力 DIN 53504

100%應變, 73°F (23°C) 4, 5 218psi 1.50MPa

300%應變, 73°F (23°C) 6, 7 363psi 2.50MPa

抗張強度 DIN 53504

流量 : 斷裂, 73°F (23°C) 6, 5 870psi 6.00MPa

橫向流量 : 斷裂, 73°F (23°C) 1870psi 12.9MPa

伸長率 4 DIN 53504

橫向流量 : 斷裂, 73°F (23°C) 650% 650%

流量 : 斷裂, 73°F (23°C) 5 450% 450%

硬度 額定值(英制) 額定值(公制) 測試方法

肖氏硬度 (邵氏 A, 3 秒) 50 50 DIN 53505

充模分析 額定值(英制) 額定值(公制) 測試方法

表觀粘度 (392°F (200°C), 11200 sec^-1) 40.4Pa·s 40.4Pa·s 內部方法

注射 額定值(英制) 額定值(公制)

建議的最大回制料比例 20% 20%

料筒后部溫度 380 到 400°F 193 到 204°C

料筒中部溫度 390 到 420°F 199 到 216°C

料筒前部溫度 400 到 440°F 204 到 227°C

射嘴溫度 410 到 460°F 210 到 238°C

加工（熔體）溫度 400 到 440°F 204 到 227°C

模具溫度 55.0 到 90.0°F 12.8 到 32.2°C

背壓 0.00 到 80.0psi 0.00 到 0.552MPa

螺桿轉速 50 到 100rpm 50 到 100rpm

 

 

GLS 422-126

熱塑性彈性體

吉力士（GLS）公司，熱塑性彈性體部門

 

注射說明

Color concentrates based on polypropylene (PP), ethylene vinyl acetate (EVA), or low density polyethylene (LDPE) are most suitable for coloring GLS 422-126. Improved color dispersion can be achieved by using higher melt flow concentrates (with a melt flow from 25-40 g/10 min). Typical loadings for color concentrates are 1% to 5% by weight. Liquid color can be used, but mineral oil based carriers may have a significant effect on the final hardness value. Concentrates based on PVC should not be used. A high color match consistency can be obtained by the use of precolored compounds available from GLS. The final determination of color concentrate suitability should be determined by customer trials.

 

Purge thoroughly before and after use of this product with a low flow (0.5 - 2.5 MFR) polyethylene (PE) or polypropylene (PP).

 

Regrind levels up to 20% can be used with GLS 422-126 with minimal property loss, provided that the regrind is free of contamination. To minimize losses during molding, the melt temperature should remain as low as possible. The final determination of regrind effectiveness should be determined by the customer.

 

GLS 422-126 has excellent melt stability. Maximum residence times may vary, depending on the size of the barrel. Generally, the barrel should be emptied if it is idle for periods of 8 - 10 minutes or longer.

 

Drying is not Required

 

Injection Speed: 1 to 3 in/sec

1st Stage - Boost Pressure: 500 to 700 psi 2nd Stage - Hold Pressure: 10 to 30% of Boost Hold Time (Thick Part): 2 to 4 sec

Hold Time (Thin Part): 1 to 2 sec

 

擠出 額定值(英制) 額定值(公制)

熔體溫度 400 到 440°F 204 到 227°C

口模溫度 420 到 460°F 216 到 238°C

擠壓說明

Rear: 380-400F

Center: 390-420F

Front: 400-440F

Screw: 100-500rpm

 

 

 

 

 

TPE GLS 422-126, 熱塑性彈性體TPE,包膠熱塑性彈性體TPE,包膠PP熱塑性彈性體TPE,包膠PA尼龍熱塑性彈性體TPE,包膠PA6熱塑性彈性體TPE,包膠PA66熱塑性彈性體TPE,包膠POM熱塑性彈性體TPE,包膠PE熱塑性彈性體TPE,包膠ABS熱塑性彈性體TPE,包膠PC+ABS熱塑性彈性體TPE,包膠PC熱塑性彈性體TPE,包膠PS熱塑性彈性體TPE,包膠ASA熱塑性彈性體TPE,包膠PMMA熱塑性彈性體TPE,包膠SAN熱塑性彈性體TPE,包膠PBT熱塑性彈性體TPE,包膠PPO熱塑性彈性體TPE,包膠熱塑性彈性體TPE是東莞市雙幫塑膠原料有限公司常年銷售的塑料,因為塑料價格行情每天都有新變化前天的報價不等于今天的報價。本公司銷售的所有原料保證是原廠原包,隨料可以提供生產廠商提供的物性表,SGS報告,COA原料出廠報告,REACH報告,SVHC報告,生物兼容報告,UL黃卡,提供原料注塑加工工程中可能出現的各種異常現象解決方法，塑料牌號太多，本網站沒有提供的本公司也有代理，詳情請咨詢本公司相關業務人員0769-87795123，微信：13549213581  QQ：15397858    13549213581 肖生