Amodel® AT-1001L    
    
聚二甲苯酰胺    
    
Solvay Specialty Polymers   
     
 Technical Data    
     

產(chǎn)品說明

Amodel® AT-1001L is an unreinforced, impact modified polyphthalamide (PPA) resin that exhibits exceptional impact strength at temperatures ranging from room temperature to as low as -40°F (-40°C), which suggests possible applications in ski boots and hockey skates.

In addition, its chemical and wear resistance, combined with good mechanical properties, make Amodel® AT-1001L resin a prime candidate for applications such as anti-friction and wear resistant components, chemical, oil field, automotive and safety equipment.

• Natural: AT-1001 L NT

總體

材料狀態(tài) • 已商用：當(dāng)前有效   
資料 1 •  Technical Datasheet
  
搜索 UL 黃卡 •  Solvay Specialty Polymers
  
 •  Amodel®
  
    
供貨地區(qū) • 北美洲 • 南美洲 • 亞太地區(qū) 
 • 非洲和中東 • 歐洲  
    
添加劑 • 沖擊調(diào)節(jié)器 • 潤滑劑 • 脫模 
 • 低翹曲性 • 耐低溫撞擊 • 透濕性強(qiáng) 
性能特點(diǎn) • 改良抗撞擊性 • 耐化學(xué)性良好  
   • 延展性 
 • 經(jīng)潤滑 • 耐磨損性良好  
    
 • Oil/Gas Applications • 金屬置換 • 設(shè)備/機(jī)械部件 
用途 • 工業(yè)領(lǐng)域： • 汽車電子 • 型號 
 • 工業(yè)配件 • 汽車領(lǐng)域的應(yīng)用： • 一般目的 
RoHS 合規(guī)性 • 聯(lián)系制造商   
外觀 • 自然色   
形式 • 顆粒料   
加工方法 • Water-Heated Mold Injection • 注射成型  
 Molding   
    
 
多點(diǎn)數(shù)據(jù) • Isothermal Stress vs. Strain 
 (ISO 11403-1) 
  
 

• Secant Modulus vs. Strain (ISO 11403-1)
 

物理性能 額定值單位制 測試方法
密度 1.11g/cm³ ISO 1183/A
收縮率  ASTM D955
流動 1.7 到 2.2% 
橫向流動 1.9 到 2.1% 
吸水率 (24 hr) 0.75% ASTM D570
機(jī)械性能 額定值單位制 測試方法
拉伸模量 1900MPa ASTM D638
抗張強(qiáng)度 (斷裂) 62.1MPa ASTM D638
伸長率  ASTM D638
屈服 6.0% 
斷裂 30% 
彎曲模量 2210MPa ASTM D790
彎曲強(qiáng)度 96.5MPa ASTM D790
泊松比 0.35 ASTM E132
沖擊性能 額定值單位制 測試方法
懸壁梁缺口沖擊強(qiáng)度  ASTM D256
-40°C 750J/m 
23°C 1100J/m 
熱性能 額定值單位制 測試方法
熱變形溫度 (1.8 MPa, 退火, 3.18 mm) 120°C ASTM D648
熔融溫度 310°C 

 
 
 
 
 
 
 
Amodel® AT-1001L      
聚二甲苯酰胺      
      
Solvay Specialty Polymers   
        
  補(bǔ)充信息      
        
  Penetration Impact, ASTM D3763, 73°F, Maximum Load: 1100 lbs      
  Penetration Impact, ASTM D3763, 73°F, Total Energy Absorbed: 40 ft-lbs      
  Penetration Impact, ASTM D3763, 73°F, Energy to Maximum Load: 30 ft-lbs      
  Penetration Impact, ASTM D3763, -10°F, Total Energy Absorbed: 40 ft-lbs      
  Penetration Impact, ASTM D3763, -10°F, Maximum Load: 1260 lbs      
  Penetration Impact, ASTM D3763, -10°F, Energy to Maximum Load: 30 ft-lbs      
     
  注射  額定值單位制 
  干燥溫度  110°C 
  干燥時間  4.0hr 
  建議的最大水分含量  0.045%    
  料筒溫度  79.4°C 
  螺筒后部溫度 304 到 318°C 
  螺筒前部溫度 316 到 329°C 
  加工（熔體）溫度 321 到 343°C 
  模具溫度 65.6 到 110°C